Elcometer 3230 湿膜轮
如果知道涂层的干、湿比率，便可通过湿膜厚度计算干膜厚度。
不同的测量量程从0~25μm（0~1mils）*0~3000μm（0~40mils）。

连续刻度，测量准确度为±5%。
适用于平面和曲面测量。
不锈钢材质，耐磨损，用溶剂清洗后可重复使用。

Elcometer 3230 湿膜轮

型号	分类	量程	分度	零件号
Elcometer 3230/1	Elcometer 3230 湿膜轮	0~25μm	1.25μm	K0003230M001
Elcometer 3230/16	Elcometer 3230 湿膜轮	0~40μm	2.0μm	K0003230M016
Elcometer 3230/2	Elcometer 3230 湿膜轮	0~50μm	2.5μm	K0003230M002
Elcometer 3230/3	Elcometer 3230 湿膜轮	0~100μm	5.0μm	K0003230M003
Elcometer 3230/4	Elcometer 3230 湿膜轮	0~150μm	7.5μm	K0003230M004
Elcometer 3230/5	Elcometer 3230 湿膜轮	0~200μm	10.0μm	K0003230M005
Elcometer 3230/6	Elcometer 3230 湿膜轮	0~250μm	12.5μm	K0003230M006
Elcometer 3230/7	Elcometer 3230 湿膜轮	0~300μm	15.0μm	K0003230M007
Elcometer 3230/8	Elcometer 3230 湿膜轮	0~400μm	20.0μm	K0003230M008
Elcometer 3230/9	Elcometer 3230 湿膜轮	0~500μm	25.0μm	K0003230M009
Elcometer 3230/10	Elcometer 3230 湿膜轮	0~1000μm	50.0μm	K0003230M010
Elcometer 3230/15	Elcometer 3230 湿膜轮	0~1500μm	75.0μm	K0003230M015
Elcometer 3230/11	Elcometer 3230 湿膜轮	0~2000μm	100μm	K0003230M011
Elcometer 3230/12	Elcometer 3230 湿膜轮	0~3000μm	150μm	K0003230M012
Elcometer 3230/1a	Elcometer 3230 湿膜轮	0~1mils	0.05mils	K0US3230M001
Elcometer 3230/2a	Elcometer 3230 湿膜轮	0~2mils	0.1mils	K0US3230M002
Elcometer 3230/3a	Elcometer 3230 湿膜轮	0~4mils	0.2mils	K0US3230M003
Elcometer 3230/4a	Elcometer 3230 湿膜轮	0~6mils	0.25mils	K0US3230M004
Elcometer 3230/5a	Elcometer 3230 湿膜轮	0~12mils	0.5mils	K0US3230M005
Elcometer 3230/6a	Elcometer 3230 湿膜轮	0~20mils	1mils	K0US3230M006
Elcometer 3230/7a	Elcometer 3230 湿膜轮	0~40mils	2mils	K0US3230M007
附件	15cm（5″）湿膜轮手柄			KT003230N003
	50cm（19″）湿膜轮手柄			KT003230N002
	100cm（39″）湿膜轮手柄			KT003230N001

Elcometer 3230 湿膜轮

符合以下标准
ASTM D1212-91-A	BS 3900-C5-1B
ISO 2802-1B	NF T30-125

How to use a Wet Film Wheel - Elcometer 3230 Wet Film Wheel

ISO 2808-7B, BS 3900-C5 method 7B, ASTM D4414-A specify that the wet film wheel should be perpendicular to the substrate and the thickness of the coating should be stated as that indicated on the central wheel - ensuring that the wheel has been rolled from maximum thickness to minimum thickness - thus avoiding surface tension.

Example

Hold the wheel by its central spindle. Begin at maximum thickness to reduce risk of inaccuracy caused by surface tension.

Roll the wheel through the wet film with the side 1 in the diagram touching the substrate. Roll for at least one whole turn and slowly enough for wetting to occur. Roll the wheel backwards by at least on complete turn. The wet film thickness is read from the scale, at the end of the wetted segment of the middle circle, 2 in the diagram

To use wheel on pipes, measure across the longitudinal axis (lengthways) of the pipe.

On rough surfaces, measurements will be made from the surface peaks and represent the minimum wet film thickness